1. The longitudinal tear in the middle of the steel belt is 14-15 meters, how to repair it?
The upper and lower covering glue of the damaged part can be peeled off (the length exceeds the damaged part by 50-100mm, and the width exceeds the damaged part by 30-50mm), and at the same time, take a piece of rubber with the same size as the peeled part (preferably with a layer of cloth), and then It can be repaired according to the cold glue method.
2. Comparison of EP high temperature resistant belt and cotton canvas high temperature resistant belt:
a. The same point: the surface covering glue is the same.
b. Differences: cotton canvas can withstand a maximum temperature of 150 degree ; EP-TNG canvas can be used for a long time at 200 degree , and can be used at a maximum of 220 degree ;
The strength of cotton canvas is relatively low, only 50N/mm; while the strength of EP-TNG canvas is relatively high, and the commonly used type 200 is 200N/mm;
Przyczepność paska odpornego na wysokie temperatury z płótna bawełnianego jest stosunkowo niska, a przyczepność paska odpornego na wysokie temperatury EP jest stosunkowo wysoka; żywotność pasa odpornego na wysokie temperatury EP jest oczywiście dłuższa niż pasa odpornego na wysokie temperatury z płótna bawełnianego.
3. Hot glue stripping method (is it good to remove the glue at one end)?
To kolejna metoda klejenia, ta metoda jest również możliwa, ale jeśli korzystasz z tej metody, zwróć uwagę na następujące punkty:
a. Be sure to use sealing glue;
b. The parts where the edge rubber parts meet must be connected by vulcanized rubber;
c. The parts where the rubber is connected must be polished
The disadvantage is that the edge glue part is easily damaged if it is not handled properly.
4. The joint temperature reaches 120 degree , but does not reach the normal vulcanization temperature?
no. The normal vulcanization and crosslinking temperature of rubber is determined by the vulcanizing agent and accelerator in the rubber. In order to ensure the safety of rubber processing, the general manufacturer will not set the vulcanization starting temperature of the rubber used in the conveyor belt to be very low. Therefore, when the temperature reaches 120 degree , the rubber will not enter the normal vulcanization state. Therefore, at 120 degree , the quality of the conveyor belt joint will be greatly affected.
Zwykle, gdy temperatura wulkanizacji jest wyższa niż krytyczna temperatura wulkanizacji przyspieszacza i środka wulkanizującego i nie może osiągnąć normalnej temperatury wulkanizacji, można zastosować metodę przedłużenia czasu wulkanizacji, aby wulkanizacja gumy spełniała wymagania. Generalnie za każdym razem, gdy temperatura jest niższa niż 10 stopni, czas wulkanizacji wydłuża się 2-4 razy. Oczywiście ze względów wydajnościowych nie zalecamy stosowania wulkanizacji nisko-temperaturowej i długotrwałej.
5. Can core rubbers from different manufacturers be mixed?
Nie zaleca się mieszania gumy rdzeniowej różnych producentów, ponieważ skład gumy rdzeniowej różnych producentów jest różny. W gumie jest wiele rodzajów składników, a niektóre z nich reagują interaktywnie. W formule tego samego producenta nie będzie składników wywołujących niepożądane reakcje interaktywne, ale formuły różnych producentów są bardzo różne. Podczas używania mogą wystąpić interaktywne odbicia składników, które wpływają na efekt użytkowania gumy rdzenia.